Reusing silicon from end-of-life photovoltaic modules for battery anodes

Scientists in China have proposed to use recycled silicon from discarded solar cells to build anodes for batteries. They combined the recycled waste silicon powder with graphite and created a composite material that is claimed to exhibit remarkable electrochemical performance.

Scientists led by the Kunming University of Science and Technology in China have proposed to reuse silicon from discarded solar cells to develop silicon-carbon composite anode materials that could be used in battery anodes.

“The purpose of our work was to propose a simple and effective recycling method aimed to realize the value-added reuse of silicon materials in end-of-life PV modules,” the research’s lead author, Shaoyuan Li, told pv magazine. “According to current conventional technical methods such as acid and alkali leaching, a tonne of end-of-life PV modules can recover 40 kg silicon material, which can generate a net income of $104.9. If the recycled silicon material is combined with graphite using a simple ball milling process to obtain a silicon-carbon composite anode, it can generate a revenue of $1,883.”

In the study “High-performance silicon carbon anodes based on value-added recycling strategy of end-of-life photovoltaic modules,” published in Energy, the researchers explained that the waste silicon powder (W–Si) needed for the battery anodes was obtained by pulverizing solar cell fragments with a vibration mill.

The cells had been previously mechanically dismantled from the modules and then cut into 6 mm x 6 mm fragments. These fragments were then soaked in a toluene solution for 24 h to dissolve the ethylene vinyl acetate (EVA) encapsulant. “To further remove EVA, the EVA-wrapped cell fragments were placed in a tube furnace for pyrolysis at 550 C for 2 h under the argon atmosphere,” they said. ” Deionized water and ethanol were used for ultrasonic cleaning several times to obtain solar cell fragments.”

With these fragments, the research group developed the waste silicon powder by combining the recycled silicon with graphite using a simple ball milling process. The resulting composite material, called W-Si-rM@G, reportedly showed remarkable electrochemical performance.

“It had an initial discharge capacity of up to 1,770 mA h g-1, maintained a good specific capacity of 913 mA h g-1 after 200 cycles at a current density of 500 mA g-1, and the average Coulombic efficiency reached 98.99%, which was only a 0.24% capacity loss,” Li explained, noting that the use of graphite created a buffer space for the volume expansion of silicon, which enhanced the cycling stability of the material. “Graphite had good contact with silicon particles, and the introduction of graphite greatly enhanced the electrical conductivity of the silicon material.”

Looking forward, the scientists said additional work is needed to build up a full and efficient value-added recycling industry for end-of-life PV modules, stressing the current difficulties of setting up profitable businesses in this sector without public support. “The recycling of end-of-life PV modules has certain economic feasibility, but it is not economical enough to maintain the smooth operation of an enterprise,” they stated.

This post appeared first on PV Magazine.

Share This Post